2016 AIChE Annual Meeting

(505h) Reversible Assembly of Colloidal Particles Using Low Frequency Pulsed DC Electric Fields for Electrophoretic Displays

Authors

Andrew J. Pascall - Presenter, Lawrence Livermore National Laboratory
Elaine Lee, Lawrence Livermore National Laboratory
Hannah Coe, Lawrence Livermore National Laboratory
Brian Giera, University of California Santa Barbara
Marcus Worsley, Lawrence Livermore National Laboratory
Joshua D. Kuntz, Lawrence Livermore National Laboratory
Luis A. Zepeda-Ruiz, Lawrence Livermore National Laboratory
We present the reversible assembly of colloidal nanoparticles in organic solvents using low voltage and low frequency pulsed DC electric fields. Commercially available and custom nanoparticles (diameter ~ 50-200 nm) were suspended in organic solvents at concentrations of 0.25-50 wt% and sandwiched between indium tin oxide (ITO) electrodes of spacing 25 μm-2mm. Using square waves of frequency 0.25-5 Hz, voltages 0.5-5V, and DC offset 0.25-2.5V, colloidal suspensions were actuated for switchable contrast. Upon switching off the electric field, the assembled nanoparticles are able to resuspend within seconds. Using patterned electrodes, lateral electromigration of the particles was demonstrated. Depletion of the particles to the electrode regions resulted in transparency in the non-patterned regions. The distinct contrast generated can be exploited for tunable display applications. We will also present a particle-based numerical model of the deposition and resuspension processes.