2008 Annual Meeting

(122e) Confined Synthesis of Silicalite-1 Nanocrystals In Threedimensionally Ordered Mesoporous Carbon

Authors

Wei Fan - Presenter, University of Massachusetts - Amherst
Sandeep Kumar, University of Minnesota
Yoo won Choel, Institute of Technology, University of Minnesota
Andreas Stein, University of Minnesota
R. Lee Penn, University of Minnesota
Michael Tsapatsis, University of Minnesota
The sustained interest in the synthesis of zeolite nanocrystals is justified because they can serve as catalysts, seeds for thin film growth and for preparation of polymer-zeolite nanocomposite membranes. In this study, silicalite-1 was synthesized inside three-dimensionally-ordered mesoporous carbon with a uniform pore size that can be tuned from 20 to 40 nm. The three-dimensionally-ordered mesoporous (3DOm) carbon was prepared using ordered arrays of silica nanoparticles (Lys-Sil) as a template1,2. Electron Microscopy, X-ray diffraction and N2 adsorption and desorption reveal that the silicalite-1 nanocrystals can reliably replicate the 3DOm porosity, resulting in the first highly ordered mesopororous/microporous material with inverse opal mesoporosity and MFI zeolite microporosity. Applications in catalysis and membranes will be discussed along with implications in understanding zeolite nucleation and growth.

1. Yokoi, T.; Sakamoto, Y.; Terasaki, O.; Kubota, Y.; Okubo, T.; Tatsumi, T. J. Am. Chem. Soc. 2006, 128, 13664-13665.

2. Davis, T. M.; Snyder, M. A.; Krohn, J. E.; Tsapatsis, M. Chem. Mater. 2006, 18, 5814-5816.